ANALYSIS OF AIR PRESSURE IN ALUMINUM THERMAL SPRAY PROCESS ON ADHESION STRENGTH AND COATING THICKNESS COATING LAYER ON AISI 1020 STEEL

Authors

  • Moh. Yusron Fillah Student
  • Sri Hastuti Universitas Tidar
  • Nurhadi Universitas Tidar
  • Adityo Noor Setyo Hadi Darmo Universitas Tidar

DOI:

https://doi.org/10.34128/je.v12i1.284

Keywords:

thermal spray AL, AISI 1020, Coating, air pressure

Abstract

The thermal spray aluminum (TSA) coating method is used to prevent damage to the metal surface and improve the quality of the metal surface by bonding the coating. The coating standard has a minimum thickness of 80-100 µm. According to AWS C2.23M/C2.23, NACE N0.12, SSPC CS-23, coatings submerged in seawater will experience a decrease in coating thickness of 20 µm. This study aims to examine the effect of air pressure in the thermal spray coating process on AISI 1020 steel on the bond strength of the coating to the base metal. The research was conducted using air pressure variations of 3 Bar, 3.5 Bar, and 4 Bar. Furthermore, dry film thickness, pull off adhesive, and bending tests were conducted. The dry film thickness test results show that the higher the air pressure, the coating thickness increases. The results of the pull off adhesive test show that the higher the air pressure the bonding strength of the coating also increases. The bending test results show results that are in accordance with standard practice item No.21100 where there are no cracks and small cracks are still allowed.

References

E. Budiyanto, D. A. Setiawan, H. Supriadi, and K. Ridhuan, “Pengaruh Jarak Anoda-Katoda pada Proses Elektroplating Tembaga Terhadap Ketebalan Lapisan dan Efisiensi Katoda Baja AISI 1020.,” TURBO, vol. 5, 2016.

Muhammad Sulton Ali, Herman Praktikno, and Wimala L. Dhanistha, “Analisis Pengaruh Variasi Sudut Blasting dengan Coating Campuran Epoxy dan Aluminium Serbuk terhadap Kekuatan Adhesi, Prediksi Laju Korosi, dan Morfologi pada Plat Baja ASTM A36,” JURNAL TEKNIK ITS, vol. 8, 2019.

Suyitno, Bahan Teknik untuk Rekayasawan (Logam Ferro). yogyakarta: pustaka pranala, 2022.

Muslih Nasution and Rini Halila Nasution, “Analisa Kekerasan dan Struktur Mikro Baja AISI1020 terhadap Perlakuan Carburizing DENGAN Arang Batok Kelapa,” Buletin Utama Teknik , vol. 5, 2020.

W. B. Santosa, R. B. Bungkang, and O. Mursid, “Analisa Pengaruh Metode Hot Dip Galvanizing Dengan Variasi Temperatur dan Waktu Pencelupan Terhadap Laju Korosi Pipa Air Laut Kapal Material Baja AISI 1020,” TEKNIK, vol. 43, no. 2, pp. 202–210, Aug. 2022, doi: 10.14710/teknik.v43i2.45612.

Rochman R, Hariyati P, and Purbo C, “Karakterisasi Sifat Mekanik dan Pembentukan Fasa Presipitat pada Aluminium Alloy 2024–T81 Akibat Perlakuan Penuaan,” MEKANIKA, vol. 8, no. 2, 2010.

D. Fajar Fitriyana, G. Dwi Haryadi, N. Iskandar, and A. Gilang Amrizal, “Pengaruh Jarak Penembakan pada Pelapisan 95MXC Terhadap Sifat Kekerasan dan Keausan Material SS 304 dengan metode Twin Wire Arc Spray (TWAS),” 2018.

P. Vuoristo, Thermal Spray Coating Processes, 1st ed., vol. 4. D. Cameron (Ed.): Elsevier, 2014.

D. Fajar Fitriyana, S. Nugroho, and M. Rizal Barutama, “Pengaruh Tekanan Udara Pada Proses Pelapisan 95MXC Dengan Metode Twin Wire Arc Spray Terhadap Kekerasan dan Ketahanan Aus Pada Stainless Steel 304,” vol. 23, no. 1, pp. 59–63, 2021.

ISO 8501, “Preparation of steel substrates before application of paints and related products Visual assessment of surface cleanliness.” 2007

ASTM D4138, “Standard Test Methods for Measurement of Dry Film Thickness of Protective Coating Systems by Destructive Means 1,” 2001

ASTM D4541, “Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers 1,” 2022 doi: 10.1520/D4541-22.

Standard Practice Item No. 21100, “Specification for the Application of Thermal Spray Coatings (Metallizing) of Aluminum, Zinc, and Their Alloys and Composites for the Corrosion Protection of Steel,” 2016.

ASM International, Hand Book Thermal Spray Technology. 2004.

M. A. Hidayanto et al., “Pengaruh Voltage pada proses Thermal Spray Aluminium terhadap Kekuatan Ikatan Lapisan Coating pada Baja ST 60,” vol. 6, no. 2, 2023.

American Welding Society C2.23M/C2.23, “Specification for the Application of Thermal Spray Coatings (Metallizing) of Aluminum, Zinc, and Their Alloys and Composites for the Corrosion Protection of Steel,” 2018 [Online]. Available: www.copyright.com

Published

2025-06-28

How to Cite

Fillah, M. Y., Hastuti, S., Nurhadi, & Darmo, A. N. S. H. (2025). ANALYSIS OF AIR PRESSURE IN ALUMINUM THERMAL SPRAY PROCESS ON ADHESION STRENGTH AND COATING THICKNESS COATING LAYER ON AISI 1020 STEEL. ELEMEN : JURNAL TEKNIK MESIN, 12(1), 1–9. https://doi.org/10.34128/je.v12i1.284

Issue

Section

Author guidelines

Similar Articles

1 2 3 4 5 6 7 8 > >> 

You may also start an advanced similarity search for this article.