STRENGTH ANALYSIS OF SMAW WELDING BUTT JOINT ON ST-37 MATERIAL WITH VARIATION OF ELECTRODE AND WELDING SPEED

Authors

  • Deni Pamungkas Universitas Tidar
  • Sri Hastuti Universitas Tidar
  • Ikhwan Taufik Universitas Tidar

DOI:

https://doi.org/10.34128/je.v11i1.277

Keywords:

kecepatan pengelasan, kekuatan tarik, AWS E 7016, AWS E 6013

Abstract

Shield Metal Arc Welding (SMAW) welding in practice often faces challenges in the form of defects in the joints which damage the quality of the connection. One implementation of welding connections is the process of making a paddock. Poor welding can damage the paddock and harm its users. The research aims to determine the effect of welding speed and electrodes on the tensile strength, hardness and microstructure of ST-37 steel welded joints. The research used AWS E 7016 and AWS E 6013 electrodes with a current of 100 amperes and varying welding speeds of 0.2 cm/s, 0.3 cm/s and 0.4 cm/s. The highest tensile strength for the AWS E 7016 electrode was 460.32 MPa and the lowest for the AWS E 6013 electrode was 256.02 MPa. The highest hardness value on AWS E 7016 was 236.07 MPa and the lowest was on AWS E 6013, amounting to 176.86 MPa. The ferrite composition dominates the weld metal. Because ferrite is ductile and not too hard, it means that the weld metal area is ductile and the hardness is not too high.

References

I. Afrianto Rabbi, “Analisa Pengaruh Gerakan Elektroda pada Pengelasan SMAW terhadap Uji Kekerasan dan Kekuatan Bending Baja ST 37,” Semin. Nas. Ind. dan Teknol., hal. 131–149, 2018.

H. Rashid, A. H. Abdullah, M. H. Mohd Noh, A. H. Abdul Hamid, dan N. M. Zainal Abidin, “Design of a superbike paddock stand using cad and cae tools,” Int. J. Automot. Mech. Eng., vol. 5, no. 1, hal. 670–679, 2012, doi: 10.15282/ijame.5.2012.13.0054.

T. C. Agency et al., “No Title Πώς Παράγονται και Παρέχονται Αποτελεσματικά Υπηρεσίες Ποιότητας,” Transportation (Amst)., vol. 1, no. January, hal. 21–30, 2006, doi: 10.1002/ejoc.201200111.

Azwinur, A. S. Ismy, R. Nanda, dan Ferdiyansyah, “Pengaruh arus pengelasan SMAW terhadap kekuatan sambungan las double lap joint pada material AISI 1050,” J. Weld. Technol., vol. 2, no. 1, hal. 1–7, 2020.

H. Ivandri, I. P. Mulyatno, dan Kiryanto, “Analisis Pengaruh Variasi Sudut Kampuh Double V Pada Sambungan Las SMAW (Shield Metal Arc Welding) Baja St 37 Terhadap Kekuatan Tarik, Tekuk dan Impact,” J. Tek. Perkapalan, vol. 5, no. 4, hal. 785, 2017, [Daring]. Tersedia pada: http://ejournal3.undip.ac.id/index.php/naval

Tarkono, Sugiyanto, dan Andriyanto, “Studi penggunaan jenis elektroda las yang berbeda terhadap sifat mekanik pengelasan SMAW Baja AISI 1045,” J. Mech., vol. 1, no. 1, hal. 51–62, 2010.

R. A. Gumara dan N. S. Drastiawati, “Pengaruh Variasi Arus Listrik Pengelasan Metal Inert Gas (MIG) Terhadap Kekuatan Tarik Sambungan Las Pada Baja Karbon ASTM A36,” Jtm, vol. 09, no. 03, hal. 65–68, 2021.

M. Javed, A. Khalid Hussain, dan A. Lateef, “Influence of Welding Speed on Tensile Strength of Welded Joint in TIG Welding Process,” Int. J. Appl. Eng. Res., vol. 1, no. 3, hal. 518–527, 2010.

C. Journal dan B. E. Vol, “2 2 2 Π,” no. 30, hal. 56–70, 2006.

A. S. Mohruni dan B. H. Kembaren, “Struktur Mikro Baja Karbon Rendah Dengan Elektroda E6013,” vol. 13, no. 1, hal. 1–8, 2013.

H. Bisri dan Y. Yunus, “Pengaruh Media Pendingin Pada Proses Pengelasan SMAW Material Baja SS400 Terhadap Kekuatan Tarik dan Struktur Mikro Yunus Abstrak,” J. Tek. Mesin Unesa, vol. 10, no. 03, hal. 55–60, 2022.

Anang Setiawan dan Yusa Asra Yuli Wardana, “Analisa Ketangguhan dan Struktur Mikro pada Daerah Las dan HAZ Hasil Pengelasan Sumerged Arc Welding pada Baja SM 490,” J. Tek. Mesin, vol. 8, no. 2, hal. 57–63, 2006, [Daring]. Tersedia pada: http://puslit2.petra.ac.id/ejournal/index.php/mes/article/view/16525

I. Naryono dan F. Rakhman, “Pengaruh Variasi Kecepatan Pengelasan Pada Penyambungan Pelat Baja Sa 36 Menggunakan Elektroda E6013 Dan E7016 Terhadap Kekerasan, Struktur Mikro Dan Kekuatan Tariknya,” vol. 5, no. 2, hal. 1–13, 2012.

H. Helanianto, E. Epriyandi, dan H. Rahmadi, “Pengaruh Variasi Arus Pengelasan Smaw Terhadap Kekerasan Logam Induk Dan Logam Las,” Elem. J. Tek. Mesin, vol. 7, no. 2, hal. 138–147, 2020, doi: 10.34128/je.v7i2.148.

Y. E. Muhammad Farid Anshori, Suharno, “Jurnal Pendidikan Teknik Mesin,” Nozel, vol. 01, no. 01, hal. 09–22, 2019.

Published

2024-06-28

How to Cite

Pamungkas, D., Hastuti, S., & Taufik, I. (2024). STRENGTH ANALYSIS OF SMAW WELDING BUTT JOINT ON ST-37 MATERIAL WITH VARIATION OF ELECTRODE AND WELDING SPEED. ELEMEN : JURNAL TEKNIK MESIN, 11(1), 29–35. https://doi.org/10.34128/je.v11i1.277

Issue

Section

Author guidelines

Similar Articles

<< < 1 2 3 4 5 > >> 

You may also start an advanced similarity search for this article.